激光银浆DLS-70

silver conductor dls-70

conductive paste for laser etching of touch screen panel

product deｓｃｒｉｐｔion

dls-70 is a one part, conductive paste designed primarily for the purpose of laser etching. it can be used with semi-automatic, and manual printers, and offers excellent residence time on the screen. the cured film has excellent electrical and mechanical properties with good adhesion to a variety surfaces(ito coated film). 

processing procedures

application

before use, take paste out of the refrigerator, leave it in a room in the sealed state for approximately one hour, then use after mixing well.

the material may be applied by screen printing, a 325 or 400mesh screen with a 6-10um organic emulsion backing is recommended. use a hard silicone squeegee. screens can be cleaned with organic solvents such as 1st ethyl carbitol, 2nd  ethanol or isopropyl alcohol.

dilute solution

butyl carbitol acetate.(cas : 124-17-4)

curing

minimum cure is 130℃ for 30 minutes. cure time is only a guide. optimum conditions will vary depending upon application and will need to be determined experimentally.

storage

dls-70  should be stored frozen until ready for application. the shelf life is 4 months(0℃ ~ 5℃) from date of manufacture.

specification data

items value remarks

silver content 70±2％ tga

particle size d50 0.5~1.0㎛ psa

viscosity

(cps) 10rpm 80,000~100,000 brookfield 

hbt-dvii 
sp#14 

@ 25 ± 0.5℃

ti(5/50) 4.0 ± 1.0　

volume resistance1 2.0 ≤ ×10-4ωcm -

adhesion cross cut2 ≥ 5b 　 astm d3359

pencil hardness3 ≥ 2h -

printability4 continuous ≥ 150 times 325mesh,18㎛

400mesh,18㎛

emulsion:6~10㎛

thickness 5~8㎛

laser etching image printing 3d image

test condition

1. printed samples cured at 130℃ for 30 minutes on glass.

2, 3. printed samples cured at 130℃ for 30 minutes on ito coated pet film.

4. the original designed value of the printing mask :   line width 2mm.